Techniken und Ausstattung


Friction Stir Welding (FSW)

Friction Stir Welding

Friction stir welding (FSW) is a solid state joining process, which was developed and patented in 1991. And represent’s one of the core competences where Hereon has taken an international leading position. Such processes allow to a very high degree of freedom to weld similar and dissimilar materials, which can not be treated by any other method.

The process runs below the melting temperature of the workpiece material the heat is generated through friction and shear forces between Tool and material to be welded. The joint is built by rotational and transversal motion of the FSW tool along the abutting edges of the workpiece. It consists of the shoulder and the probe, which generate the needed heat and to stir the workpiece material, respectively create the weld joint.

Principles of the process
The steps during friction stir welding can be described as followed.
1. The tool starts to rotate and moves toward workpiece
2. The probe gets into contact and begins to plunge into the workpiece. Hereby friction and shear forces (plastic work) generate heat which plastizises (softens) the workpiece below the shoulder and around the probe
3. The tool travels in the direction of the abutting edges. Hereby the plastizised material is stirred around the tool joining the to plates
4. Tool moves out of the workpiece. The materials cool down, the weld is build and an exit hole is left

The main process parameter are the rotational speed, the welding speed and downward force (pressure) of the FSW tool.

FSW Welding Technologies are of interest of the aircraft, aerospace, automotive, locomotive, shipbuilding industry were the advantages of the process (e.g.: high joint strength, low distortion, weight neutrality and process automatisation, no material addition, no shielding gas for Aluminum and Magnesium no fume) are beneficial. In comparison to conventional fusion welds, FSW has many advantages such as: lower temperatures required to weld, environmentally clean process, low distortion and residual stress, greater weld strength, little or no porosity, little or no post weld repair, no solidification cracking, no welding fumes, improved corrosion resistance, no need for consumables and no spatter.

Stationary Shoulder Friction Stir Welding (SSFSW)


A variant, or more correctly a development, of the conventional FSW have been obtained with the use of a stationary shoulder, originally in the case of titanium weldments. The main difference between the two technologies is due to the mechanical separation between the shoulder and the probe, allowing for the shoulder not to be rotating as shown in.

Differently from conventional FSW, where the major of the heat, necessary in order to obtain the joining, is generated by the friction between the shoulder and the top surface of the material, in case of SSFSW the shoulder has just the function to retain the plasticised material in the correct position, giving a small contribution to the heat generation. Due to this the heat is distributed more uniformly throughout the thickness of the material leading to a more homogenous crystallographic structure.
Aditional Adwantages of the SSFSW are:

  • Produces welds with a excellent surface finish
  • Lower distortion due to the uniform heat input
  • Low Energy input and reduced volume of material affected by the weld
  • T Joint = Corner Joints to weld reenforcements to a Panel, Aircraft Skin Stringer Profiles

A solution in order to reduce weight in modern aircraft is the use of welding technologies to replace rivets in skin-stringer joints.

Bobbin Toll Friction Stir Welding (BT-FSW)


The Bobbin Tool variant uses a two-shoulder tool system and avoids the need of a backing plate while eliminating roots defects by full penetration of the material. Further advantages are low process forces and distortion due to a symmetrical heat input. This set-up allows welding of hollow structures like extrusions, pipes or tanks.

The machine set-up is identical to FSW and the tool consists of an upper and a lower shoulder.

Friction Stir Processing (FSP)


Friction stir processing (FSP) is a derivative of friction stir welding (FSW) and is a processing method to locally modify the microstructure and texture of a given material. Using appropriate processing parameters, the resulting material properties can be tuned to fit a specific purpose i.e. homogenization and refinement of an as-cast microstructure, or alteration of the microstructure in such ways that enhanced strength or ductility can be reached.

Principles of the technique
The tool is prepositioned at the initiation site which is to be processed (a). Consequently, the tool in set under rotation and introduced into the material (b). Via friction, the material beneath the tool is heated up and plasticized. Once a sufficient plasticization is reached, the translation motion is started (c) and the process zone created. Finally, the tool is retracted from the sample sheet (d).

Potential Applications
Grain refinement / Homogenization:
Friction stir processing can be used to homogenize an as cast microstructure locally, so that connection parts or sealing surfaces can easily be improved. The final microstructure unusually incorporates small, recrystallized grains without the occurrence of pores. The processed material usually has a higher strength compared to the base material.

Friction Spot Joining (FSpJ)

Goushegir Technique Description

Since its introduction in 2009, Friction Spot Joining (FSpJ) has shown high performance in producing polymer-metal hybrid structures. Therefore, this technique is being investigated to join lightweight alloys such as aluminium and magnesium with high performance engineering thermoplastics and composites. For this reason a friction spot welding / joining machine (RPS 100) is employed. Briefly, the metallic partner is plasticized and deformed due to the generated frictional heat and applied force. A metallic nub is created which is inserted into the composite. Simultaneously, a thin layer of polymer matrix is molten, and displaced around the joining area. The joint is formed after consolidation of the polzmeric molten layer. These are the two main phenomena responsible for joining mechanisms.

The term "joining" is used to differentiate spot joints where a sharp interface is present (minimal or absent atomic or molecular diffusion), such as in hybrid polymer-metal joints, while "welding" is used for joints without a discontinuous transition between joining partners (presence of diffusion mechanisms), such as "polymer-polymer" or "metal-metal" spot welds.

Read more about principles of Friction Spot Joining (PDF) (328 KB)

Friction Spot Welding (FSpW)


Friction Spot Welding or also known as Refill Friction Stir Spot Welding is a solid-state welding process developed and patented by Helmholtz-Zentrum Hereon GmbH. The process was developed as an alternative to riveting or resistance spot welding to produce similar and dissimilar overlap joints.

Refill FSSW uses a non-consumable tool consisting of three independent movable parts, including a stationary clamping ring and two rotating parts of the sleeve and the probe, as presented in Figure 1. The principles of the Refill FSSW are presented in Figure 2 and 3. First, the process starts with the clamping ring moving downwards to fix the workpiece for the rest of the process. Sleeve and probe start to rotate under a pre-set speed. Following that, in the sleeve plunge variant the sleeve plunges downwards into the workpiece while the probe is simultaneous retracted. The rotating sleeve generates frictional heat plasticizing the workpiece material. The downward movement of the sleeve forces the softened material into the cavity left by the probe. When a pre-determine plunge depth is reached, the rotating pin and sleeve move back to their initial position, pushing the material back into the joint to refill the keyhole left by the retracting sleeve. At the interface between the refilling plasticized material and the surrounding workpiece, metallic bonding is created by diffusion processes over the interface. In probe plunge variant as shown in Figure 3, the rotating probe plunges into the materials while the probe is simultaneous retracted. Finally, the tool is retracted from the surface, leaving a spot weld without a keyhole, as presented in Figure 3. Additionally, the Refill FSSW is also an excellent technique for closing keyhole, such as in conventional friction stir welding, by applying plug material.

This technique has successfully been used to produce overlap joints in different materials in similar and dissimilar joint configuration, such as aluminum-aluminum, magnesium-magnesium, aluminum-steel, magnesium-steel, aluminum-titanium, and magnesium-titanium.

Friction Riveting (FricRiveting)

Blaga Technique Description

Friction Riveting (Fricriveting), is an innovative joining technique for polymer-metal hybrid structures, developed and patented by the Helmholtz Zentrum Geesthacht in Germany. In this process, polymeric parts are joined by a metallic rivet; the joining is achieved by mechanical interference and adhesion between the metallic and polymeric joining partners. During the process, a rotating cylindrical metallic rivet is inserted into a polymeric base plate. Due to the local increase of temperature, a molten polymeric layer is formed around the tip of the rotating rivet. The local temperature increases leading to the plasticizing of the tip of the rivet. While the rotation is being decelerated, the axial pressure is increased, the so called forging pressure is applied and the plasticized tip of the rivet is being deformed and anchored in the polymeric plate. The technology is adequate to produce overlap riveted joints between metal-polymer, metal-composite and composite-composite connections.

Read more about principles of Friction Riveting (PDF) (74 KB)

Injection Clinching Joining (ICJ)

Abibe Technique Description

Injection Clinching Joining (ICJ) is a new joining process for hybrid structures, composed of one thermoplastic-based partner and a metallic or thermoset partner. The principle of the process is to produce joints through heating and deformation of a thermoplastic element (such as a cylindrical stud) integrated in the polymeric partner, which is previously inserted in a through hole (cavity) of a metallic/thermoset component, therefore creating a rivet from the structure itself. Spot joints created by ICJ process are tight and with good mechanical anchoring due to the cavity profiles on the metallic partner. ICJ is a potential technology for secondary and tertiary structures in automotive and aircraft applications.

Read more information about principles of ICJ (PDF) (242 KB)

Ultrasonic Joining (U-Joining)

Eduardo Techniques

Ultrasonic joining (U-Joining) is a new direct assembly technique developed by Helmholtz-Zentrum Hereon (patent EP 3 078 480 A1). U-Joining uses ultrasonic energy to join fiber-reinforced thermoplastics to surface-structured metallic parts, for instance produced by metal injection molding (Hereon’s patent EP 2 468 436 B1). Ultrasonic vibration and pressure create frictional heat at the materials interface, which softens the composite matrix and allows the reinforcement (structured on the surface of the metallic part) to penetrate the composite. As a result, a metal-composite hybrid joint with improved out-of-plane strength is achieved.

Read more information about principles of U-joining (PDF) (261 KB)


Addjoining Aa2024 Cf-pa6

The AddJoining concept (German patent application number DE 10016121267.9) uses a new and unique approach to produce complex hybrid parts, by combining the principles of joining and polymer additive layer manufacturing (ALM) to produce layered metal-polymer hybrid structures. This is an important contribution to the state-of-the-art in additive manufacturing. AddJoining has potential to overcome the main limitations of production time of state-of-the-art manual lamination techniques, allowing for the production of future composite-metal layered structures with high-specific strength (Rm/density), tight dimensional and damage tolerances.

Read more information about principles of AddJoining (PDF) (1,1 MB)


T805 Doppelschulter (Bobbin tool) FSW Roboter System

140617 Wmp Www T805 Bbt Maschine Foto

Siemens 840D Steuerung
5 Achsen
Positionsgen. ±50µm
Wiederholgen. ±10µm
Max. Beschleunigung 2G
Max. Geschwindigkeit 90m/min
Max. Kräfte:
Vertikal : 45000 N
Horizontal: 10000 N

Hereon Flexistir Doppelschulter (Bobbin tool) FSW System

140617 Wmp Www Flexistir Maschine Foto Frontal

Sechs über Motoren kontrolliert verfahrbahre Achsen
Eine manuell justierbare Achse
Zwei unabhängig kontrollierbare Spindeln

Doppelschulter-FSW-Werkzeug (Bobbin tool, BT)
-bis zu 20Nm je Spindel
0-2000 u min^-1
-bis zu 4kN Spaltkraft

Einschulter-FSW Stahlschweißkopf:
-bis zu 80Nm
-bis zu 40kN Axialkraft

Messung und Regelung
-der axialen Kraft
-der Drehzahl

-der Axialkraft
-der Kräfte in der Ebene
-des Drehmomentes an der Spindel

Hereon Portal FSW System

140701 Wmp Www Gantry Maschine Foto Iso

Axialkräfte bis 60 kN
Seitenkräfte bis 15 kN
Kräfte in Vorschubrichtung bis 20 kN
Schweißgeschwindigkeit regelbar zwischen 0,1 und 4 m/min
Drehzahlen zwischen 200 und 6000 U/min
Maximale ununterbrochene Schweißlänge 2500 mm

Messung und Regelung
-der axialen Kraft
-der Drehzahl

-der Kräfte in der Ebene
-des Drehmomentes an der Spindel

T9000 FSW Roboter System

140617 Wmp Www T900 Robgant Maschine Foto Frontal Fischauge

Elektrischer Antrieb
Drehzahl bis 6000 U/min
Axialkräfte bis 60 kN
Radialkräfte bis 20 kN
Dimension des Arbeitsraumes 6m x 2m x 0,8m

Messung und Regelung
-der axialen Kraft
-der Drehzahl

-der Kräfte in der Ebene
-des Drehmomentes an der Spindel

Hereon RPS 100 Reibpunktschweiß System

140630 Rps100 Wmp Www Foto Frontal

Elektr. Antrieb
Drehzahlen zwischen 500 und 3000 U/min
Max. Punktdurchmesser 12mm
Max. Schweißtiefe 10mm

Messung und Regelung
-der axialen Kraft
-der Drehzahl
-des Vorschubweges von Stift und Hülse

Hereon RPS 200 Reibpunktschweiß System

140617 Wmp Www Rps200 Maschine Foto Perspektivisch

Hub des Schweißwerkzeugs: 10 mm
Schweißkraft: 35 kN
Drehmoment: 60 Nm (90 Nm für 15 s)
Drehzahl der Werkzeugelemente: 3300 rpm
Arbeitsfläche: 1000 mm x 500 mm
Masse: 4,7 t
Hub des Schweißkopfes: 300 mm
Aufspannkraft: 40 kN

Messung und Regelung:
-Drehmoment am Stift
-Drehmoment an der Hülse
-Eindringkraft des Stifts
-Eindringkraft der Hülse
-Weg Stift
-Weg Hülse

Hereon Reibauftrag- / HFDB- Schweiß System

140617 Wmp Www Ras Maschine Foto Perspektivisch

Axialkraft: 0-60 kN
Drehzahl: 0-6000 rpm
Drehmoment: max. 200 Nm
Sehr steife und robuste Konstruktion
Arbeitsraum: 0,5 m x 1,5 m x 0,3 m
Durchmesser Bolzen: max. 30 mm
Länge Bolzen: bis zu 300 mm

Messung und Regelung
-der Kräfte in drei Raumrichtungen
-des Drehmoments an der Spindel
-der Drehzahl an der Spindel
-des Vorschubweges in x-, y- und z-Achse

Hereon RSM Reibniet System (klein)

Rsm 400

Pneu./ Elektr. Antrieb
Drehzahlen zwischen 6000 und 24000 U/min
Axialkräfte bis 15 kN
Vorschubweg max. 50 mm

Messung und Regelung
-der axialen Kraft
-der Drehzahl
-des Vorschubweges (in Vorbereitung)

Hereon Reibniet System (groß)

140617 Wmp Www Fricriveting Maschine Foto Perspektivisch

Automatisiertes Drei-Achs Regelungskonzept mit vier Freiheitsgraden

Spindel: RSM 410 Harms & Wende
-bis 21000 u min^-1
-Axialkraft bis 24 kN
-Drehmoment bis 20Nm

Werkzeugwechsler für 20 Niete
Arbeitsfläche 1000 x 1500 mm

-3D piezoelektrische Kraftsensoren
-Messung der X, Y und Z Kräfte

Integrierte Positionssensorik

FEI Quanta 650 FEG Raster Elektronen Mikroskop

140617 Wmp Www Sem Quanta 650 Foto Frontal

Hochauflösendes Schottky Feld Emissions Mikroskop

Vakuum Modi:
Hochvakuum, HiVac (10^-2 bis10^-4 Pa)
Niedrigvakuum, LoVac (10 bis 200 Pa)
Erweiterter Vakuum Modus, ESEM (10 bis 4000 Pa)

Beschleunigungsspannung : 200 V bis 30 kV

Steuerstufe: euzentrische Position

Analytische Systeme: Simultanes electron backscatter diffraction (EBSD) und energiedispersiver Röntgenspektroskopie (EDS) Spektrometer

Hilfssysteme: Steuerungskamera, Schnellbeladung

Externe Systeme: 24h Notstromversorgung, antimagnetischer Rahmen, schwingungsdämpfender Tisch

Verschiedenes: Strahlverlangsamung, konzentrischer Rückstreu-Elektronen Detektor (concentric solid-state backscatter detector; CBS)